Roll over image to zoom in
Bambu Lab PAHT-CF
Price range: ₱2,299.00 through ₱3,990.00
Product Features
- Low Moisture Absorption
- Exceptional Mechanical Properties & Layer Adhesion
- High Tensile Strength
- Comes with High Temperature Reusable Spool
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- 0.6 mm Nozzle Recommended
- 0.2 mm Nozzle NOT Compatible
- Stainless Steel Nozzle NOT Recommended
- AMS 2 Pro, AMS HT & AMS Compatible
- AMS lite NOT Compatible
- Dry before Use for the Highest Print Quality
- Enclosure Printer Required
* Note: PAHT-CF is an upgraded version of PA-CF (PA-CF was discontinued).
Bambu Lab PAHT-CF
Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.
Low water absorption
With a 50% lower water absorption rate compared to normal PA-CF, Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.
Deflection from Dry to Wet
Mechanical Properties Comparison
*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.
Exceptional Z-bonding
Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF, bringing it the ability to withstand high levels of impact or stress without breaking or deforming.
Z-layer Performance
*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.
High tensile strength
Bambu PAHT-CF is designed to meet the demands of various industrial and engineering applications where high strength and durability are required.
Designed for high-temperature resistance
The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.
*The long-term temperature resistance is related to the structure and usage scenario of the model itself.
Reusable spool
Bambu PAHT-CF comes with a high-temperature resistant spool, which is not prone to deformation in the drying process. Continuing our concept of reducing plastic waste, the spool can also be reused with other Bambu refills.
Additional information
| Diameter | 1.75 mm |
|---|---|
| Net Filament Weight | 0.5 kg, 1 kg |
| Spool Material | PC + ABS (Temperature resistance 90 °C) |
| Spool Size | Diameter: 200 mm; Height: 67 mm |
| Drying Settings before Printing | Blast Drying Oven: 80 °C, 8 – 12 h |
| Printing and Storage Humidity | < 20% RH (Sealed with desiccant) |
| Bed Type | Engineering Plate, High Temperature Plate or |
| Nozzle Size | 0.4, 0.6(recommended), 0.8 mm |
| Nozzle Temperature | 260 – 290 °C |
| Bed Surface Preparation | Glue |
| Bed Temperature | 80 – 100 ° C |
| Cooling Fan | 0 – 40% |
| Printing Speed | < 100 mm/s |
| Retraction Length | 0.8 – 1.4 mm |
| Retraction Speed | 20 – 40 mm/s |
| Chamber Temperature | 45 – 60 ° C |
| Max Overhang Angle | ~ 70° |
| Max Bridging Length | ~ 40 mm |
| Support Material | Bambu Support for PA/PET |