Bambu Lab PLA Aero
₱2,449.00
Product Features
- Specialized for 3D RC Planes Printing
- Low Density and Light Weight
- Tough with Good Impact Resistance
- Matte Finish For Easy Coloring
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- Recommended to dry out before use
- All AMS Series Compatible
Bambu Lab PLA Aero
Bambu PLA Aero achieves low density and light weight by foaming at high temperatures during printing and creating small holes inside the prints. It's the perfect choice for light-weight and energy-saving prints, including unmanned aerial vehicles (UAVs), aerodynamic models, and gliders.
Foaming PLA materials (PLA Aero) have high requirements for material drying and parameter settings.
Low Density and Light Weight
Bambu PLA Aero has almost the same filament density as regular PLA, while the prints density is only 50% to 80%.
WEIGHT -50.5%
* When printing models of the same volume, PLA Aero is about half the weight of PLA Basic.
Controllable Model Density
Achieve lower density of the prints by increasing printing temperature and lowering flow rate.
* The average density of prints will vary with changes in parameters such as actual printing temperature, flow rate ratio, printing speed, model size, wall thickness and infill density.
Additional information
| Diameter | 1.75 mm |
|---|---|
| Net Filament Weight | 1 kg |
| Spool Material | ABS (Temperature resistance 70 °C) |
| Spool Size | Diameter: 200 mm; Height: 67 mm |
| Drying Settings before Printing | Blast Drying Oven: 55 °C，8 h |
| Printing and Storage Humidity | < 20% RH ( Sealed, with desiccant ) |
| Nozzle Size | 0.4, 0.6, 0.8 mm |
| Nozzle Temperature | 210 – 260 °C |
| Bed Type | Cool Plate, High Temperature Plate or |
| Bed Surface Preparation | Glue |
| Bed Temperature | 35 – 45 °C |
| Cooling Fan | Turn on |
| Printing Speed | < 180 mm/s |
| Retraction Length | 0.6 – 1.0 mm |
| Retraction Speed | 20 – 40 mm/s |
| Chamber Temperature | 25 – 45 °C |
| Max Overhang Angle | 55° |
| Max Bridging Length | 30 mm |
| Support | Support for PLA |